From aqueous silica dispersions to damp-proof porous materials

The hydrophobization of nanoparticles impacts their structuration in aqueous dispersions and how this structure resists drying stress. To understand and control this phenomenon, hydrophilic silica particles were hydrophobized directly in water using a range of organosilane precursors, with a precise control of the grafting density. The resulting nanostructure in water as well as its evolution during progressive drying was precisely analyzed by a combination of small-angle X-ray scattering (SAXS) and cryo-microscopy (cryo-TEM. 
 
At the fundamental level, because the hydrophobic character of the silica surfaces could be varied continuously through a precise control of the grafting density, we were able to study how the hydrophobic interactions change particles interactions, i.e. the way they interact with each other, and how this modifies the aggregates structures.
 
Practically, this opened a new route to tailor the final structure, the residual porosity, and the damp-proof properties of the fully dried silica. This method is much simpler and “greener” than traditional ones based on solvent exchanges or supercritical drying (aerogels). For example, regardless of the nature of the hydrophobic precursor, a grafting density of 1 grafter per nm2 optimized the interparticle interactions in solution in view to maximize the residual porosity in the dried material (0.9 cm3/g) and reduced the water uptake to less than 4% in weight compared to the typical value of 13% for hydrophilic particles (at T = 25 °C and relative humidity = 80%).
 

To know more : Hydrophobization of Silica Nanoparticles in Water : Nanostructure and Response to Drying Stress
 
Solenn Moro, Caroline Parneix, Bernard Cabane, Nicolas Sanson , and Jean-Baptiste d’Espinose de Lacaillerie, Langmuir 2017, 33, 4709.
 
link : http://pubs.acs.org/doi/abs/10.1021/acs.langmuir.6b04505


Haut de page



À lire aussi...

Foaming of transient polymer hydrogels

Foams made with complex fluids enables to obtain a very good foam stability, however such foams are usually difficult to produce and process : (...) 

> Lire la suite...

Internal field 59Co NMR study of cobalt-iron nanoparticles

The catalytic growth of carbon nanotubes by catalytic carbon vapor deposition (CCVD) can be performed on variety of Co, Fe, and Ni catalysts. It (...) 

> Lire la suite...

 

Informations Pratiques

Sciences et Ingénierie de la Matière Molle - UMR 7615

10 rue Vauquelin
75231 PARIS CEDEX 05

  • Directeur : E. Barthel
  • Directeur adjoint : J.B. d’Espinose
  • Directrice adjointe : G. Ducouret
  • Pôle gestion : F. Decuq, M.-T. Mendy et M. Hirano-Courcot
  • Communication : A. Hakopian et M. Ciccotti
  • Systèmes d’information : A. Hakopian
  • Assistant prévention : F. Martin

Comment venir ?